Repair and Regeneration Mortars

Repair and Regeneration Mortars

MALTAFER

Maltafer Malvin
Single-component protective mortar according to EN 1504-7 based on special anticorrosive hydraulic binders for damaged or new reinforcing bars, to be used before the restoration of concrete with anti-shrinkage mortars or before concrete castings.

PACKAGING: 25 kg bags - 70-bag platforms - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 1.8 kg / sqm per mm of thickness
ADHESION ON CONCRETE: 2,6 N / mm²

INTOFER

Intofer Malvin
Two-component protective cement grout according to EN 1504-7 and directive 2004/42 / EC, ready to use, anticorrosive for deteriorated or new reinforcing rods, to be used before the restoration of concrete with anti-shrinkage mortars or before concrete castings.

PACKAGING: 2 kg - 20 kg drums
USE: Indoor / Outdoor
COLOUR: Component A (powder) Grey • Component B (liquid) White
GRANULOMETRY: ≤ 0,2 mm
YIELD: 180 grams per linear meter for thickness made in the two coats of mm² with rod diam. 10

INTORIS MC

Intoris MC
Expanded fibre-reinforced concrete anti-shrinkage mortar with high mechanical strength, based on special solvent-resistant cements, according to EN 1504-3 Class R3 or R4-CC, for the restoration of deteriorated concrete and reinforcement in general of concrete, with high adhesive power on steel and concrete. Waterproof and insensitive to chemical attack, resistant to sulphates. It is suitable for fluid castings in formwork. Available in Class R3 or R4-CC. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 3 mm
YIELD: 1,900 kg are needed for 1m of mortar
EN 1542 ADHERENCE BOND: Type R3:> 1,5 MPa • Type R4:> 2,0 MPa
EN 13412 ELASTIC MODULE: Type R3:> 15 GPa • Type R4:> 20 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: Type R3: ≥40 MPa (Class R3)
• Type R4: ≥60 MPa (Class R4)

INTORIS MT

Intoris MT
Anti-shrinking, anti-carbonate, thixotropic, fibre-reinforced anti-carbonate mortar based on special resistant sulphate cements, in compliance with EN 1504-3 Class R3 or R4-CC, with high mechanical resistance and high adhesive power on steel and concrete. Waterproof and insensitive to chemical attack, resistant to sulphates. It is applied for the recovery of deteriorated concrete and the reinforcement in general of concrete. INTORIS MT is specifically thixotropic for spray or trowel restoration for vertical restoration operations. Available in R3 or R4-CC class. Available type "P" to be used without protective treatment to eliminate the armor stops. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
AVAILABILITY: R3 / R4 hardening 60 min • R3 / R4 "R" hardening 15 min
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 1,900 kg are needed for 1 m of mortar
EN 1542 ADHERENCE BOND: Type R3:> 1,5 MPa • Type R4:> 2,0 MPa
EN 13412 ELASTIC MODULE: Type R3:> 15 GPa • Type R4:> 20 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: Type R3: ≥40 MPa (Class R3) • Type R4: ≥60 MPa (Class R4)

INTORIS MT P

Intoris MT P
Anti-shrinking, anti-carbonate, thixotropic, fibre-reinforced anti-carbonate mortar based on special resistant sulphate cements, in compliance with EN 1504-3 Class R3 or R4-CC, with high mechanical resistance and high adhesive power on steel and concrete. Waterproof and insensitive to chemical attack, resistant to sulphates. It is applied for the recovery of deteriorated concrete and the reinforcement in general of concrete. INTORIS MT is specifically thixotropic for spray or trowel restoration for vertical restoration operations. Available in R3 or R4-CC class. Available type "P" to be used without protective treatment to eliminate the armour stops. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
AVAILABILITY: R3 / R4 hardening 60 min • R3 / R4 "R" hardening 15 min
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 1,900 kg are needed for 1 m of mortar
EN 1542 ADHERENCE BOND: Type R3:> 1,5 MPa • Type R4:> 2,0 MPa
EN 13412 ELASTIC MODULE: Type R3:> 15 GPa • Type R4:> 20 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: Type R3: ≥40 MPa (Class R3) • Type R4: ≥60 MPa (Class R4)

INTOBETON IN

Intobeton IN
Injection grout according to EN 1504-3 class R3-CC, based on special hydraulic binders, mineral pozzolanic additives, super fluid consistency and expansive action, specific for consolidation with injection of old and new walls, foundations and masonry bag, resistant to sulphates and volumetric stability. FPC 0925 production process certificate.

PACKAGE:25 kg sacks - 70 bags sacks - 17.50 ql
USE:Indoor / Outdoor
COLOUR:Grey
GRANULOMETRY:≤ 0.3 mm
SURRENDER:1.7 / 1.8 kg per liter of volume to be filled
ADHERENCE BOND EN 1542:> 1.5 MPa
ELECTIC MODULE EN 13412:> 15 GPa
CAPILLARY ABSORPTION EN 13057:≤ 0.5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE at 28 days EN 12190:≥ 30 MPa (Class R3)

INTOBETON BE

Intobeton BE
Premixed waterproof injection grout according to EN 1504-3 Class R3-CC based on special hydraulic binders and bentonite, with fluid consistency and expansive action, specific for difficult castings in formwork or inland, or for consolidation with injection of old masonry and new, foundations and bulkheads, resistant to sulphates and volumetric stability. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 0.3 mm
Yield: 1.7 / 1.8 kg per litre of volume to be filled
EN 1542 ADHERENCE BOND: > 1.5 MPa
EN 13412 ELASTIC MODULE: > 15 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: ≥ 30 MPa (Class R3)

INTOBETON COMPACT 

Intobeton Compact
Premixed mortar according to EN 1503-3 class R4-CC based on special hydraulic binders, mineral pozzolanic additives, with expansive action, specific for the horizontal static compaction of foundations, resistant to sulphates and volumetric stability. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Coloru: Grey
GRANULOMETRY: ≤ 1.3 mm
Yield: 17/18 per lt of volume to be filled
EN 1542 ADERENCE TIE: > 2.0 MPa
EN 13412 ELASTIC MODULE: > 20 GPa
CAPILLARY WATER ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: ≥ 45 MPa (Class R4)

INTOBETON R

Intobeton R
Cement-based mortar (curling) based on special solvent-based hydraulic binders, in accordance with EN 1504-3 Class R3-CC for the preparation of internal and external walls to be plastered, by machine or by hand application, as non-homogeneous old walls or mixed masonry, solid bricks, natural stone (tufa, sandstone, etc.), prefabricated concrete or cast in situ. FPC 0925 production process certificate.

PACKAGING: Loose in silo - 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 7/8 kg / m2 as a rough coat
EN 1542 ADHERENCE BOND: > 1.5 MPa
EN 13412 ELASTIC MODULE: > 15 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 GG EN 12190: > 25 MPa (Class R3)

INTOBETON

Intobeton
Structural high strength compaction mortar according to EN 1504-3 based on special sulphate-resistant hydraulic binders to be applied mechanically or by hand, for the reconstruction or restoration of reinforced concrete or concrete structures or as structural consolidation of old masonry . Available fibre-reinforced with a special composition of specially designed polypropylene fibres type "FR". Available in class R1 or R2 or R3 or R4 - CC. Also to be combined with the MALVIN NET structural reinforcement system, which uses pre-formed meshes, connectors and accessories in GFRP (Glass Fiber Reinforced Polymer) (* FIBRE NET), or FRP (Fiber Reinforced Polymer) networks made of AR GLASS glass fiber ( alkaline resistant) and cold-drawn AISI 304 stainless steel connectors. FPC 0925 production process certificate.

PACKAGING: Loose in silo - 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 17/18 kg / mq
COMPRESSION RESISTANCE TO 28 GG EN 12190:
• R10: ≥ 10 MPa • Class R1
• R17: ≥ 17 MPa • Class R2
• R25: ≥ 25 MPa • Class R3
• R35: ≥ 35 MPa • Class R3
• R40: ≥ 45 MPa • Class R4
ADHERENCE BOND EN 1542:
R10 / R17:> 0.8 MPa • R25 / R35:> 1.5 MPa • R40:> 2.0 MPa
EN 13412 ELASTIC MODULE: Type R25 / R35: > 15 GPa • Type R40:> 20 GPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)

INTOBETON AC

Intobeton AC
Structural high-strength compaction mortar according to EN 1504-3 based on special sulphate-resistant hydraulic binders, specifically for acidic environments, for inside and outside, to be applied by mechanical projection or by hand for reconstruction or restoration of concrete structures armed or concrete, structural consolidation of old walls, for the restoration and restoration of conduits, sewers and sewers. It does not corrode metals but protects them if it covers them completely. Available fibre-reinforced with a special "FR" polypropylene fibre composition. Available in class R2 or R3 or R4-CC. Thanks to the addition of special inorganic components, a strong acidic micro-structure forms, making it specific for applications in acidic environments. To be combined with the MALVIN NET structural reinforcement system, which uses prefabricated meshes, connectors and accessories made of GFRP (Glass Fibre Reinforced Polymer)(* FIBRE NET), or FRP (Fibre Reinforced Polymer) networks made of AR GLASS (alkaline-resistant) glass fibre and cold-drawn AISI 304 stainless steel connectors. FPC 0925 production process certificate.

PACKAGING: o - 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Inside and outside
COLOR: Grey
GRANULOMETRY: ≤ 1.3 mm
YIELD: 17/18 kg / sqm
COMPRESSION RESISTANCE TO 28 GG EN 12190:
• R17: ≥ 17 MPa • Class R2
• R25: ≥ 25 MPa • Class R3
• R35: ≥ 35 MPa • Class R3
• R45: ≥ 45 MPa • Class R4
ADHERENCE BOND EN 1542: R17: > 0.8 MPa • R25 / R35:> 1.5 MPa • R40:> 2.0 MPa
ELECTIC MODULE EN 13412 :Type R25 / R35:> 15 GPa • Type R40:> 20 GPa
CAPILLARY ABSORPTION EN 13057 :≤ 0.5 kg / (m² • h⁰'⁵)
RESISTANCE TO ACID: Unpublished test results (service simulation of more than 10 years)

INTORAS FLEX

Intoras Flex
Premixed, high -lasticity, anti-carbonate, thixotropic, water-repellent, fibro-reinforced, shrinkage compensated to EN 1504-2 and EN 998-1 based on special hydraulic binders, suitable for universal use on any compatible substrate. For the external and internal smoothing of concrete surfaces, of rustic, plastic and / or mineral coatings, of traditional or premixed plasters based on lime and cement, both new and old, even if painted, provided they are in excellent condition, of plasters that present shrinkage lesions, concrete block walls, autoclaved cellular concrete, coatings in polystyrene panels, even embossed polystyrene), polyurethane, cork, cement wood. To uniform plastered surfaces with different mortars. As a bonding base for coatings in polystyrene panels, polystyrene (also embossed), polyurethane, cork, cement wood. Used as a shave on coatings, it can be used as a decoration for MEHLVIT ELS / PLUS or AGROPOLI ELS / PLUS elastomeric water-based paint. Specific for finishing the thermal insulating plaster system (INTOTHERM). With sponged finish. FPC 0925 production process certificate.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
COLOUR: Grey / White
GRANULOMETRY: ≤ 0.6 mm
GRANULOMETRY: max type: ≤ 1.2 mm
YIELD: AS ADHESIVE • 2/3 kg / mq bonding; Full-surface bonding 4/5 kg / mq HOW TO RASANTE • 3/4 kg / mq
EN 1015-19 STEAM PASSAGE RESISTANCE COEFFICIENT: μ ≤ 10
CAPILLARY WATER ABSORPTION EN 1015-18: Class "W1"
THERMAL CONDUCTIVITY EN 1745: λ10, dry, mat = 0.35 W / mK
EN 1542 ADERENCE TIE:> 1 MPa
ABSORB. CAPILL AND WATER PERMEABILITY (w) EN 1062-3: <0,1 Kg / (m² • h⁰'⁵)
PERMEABILITY TO WATER VAPOR (SD) EN ISO 7783-2: Class I
PERMEABILITY TO CO2 (SD, CO2) EN 1062-6: > 50 m
COMPRESSION RESISTANCE At 28 days EN 1015-11: > 18 MPa (CSIV Class)
CERTIFICATION: Tested according to ETAG 004

INTORAS BICO

Intoras Bico
Two-component, anti-carbonate fibre-reinforced thixotropic shaving according to EN 1504-2 and EN 998-1, based on special hydraulic binders and special synthetic polymers, specific for the external and internal smoothing of concrete surfaces, old and new plasters, stones, bricks, tuff, rustic, plastic and / or mineral coatings. Specifically for the laying of 225 g fiberglass mesh with MALVIN NET 2.25 anti-alkali treatment, for reinforced structural reinforcement of masonry elements.

PACKAGING: 25 kg sacks - 35 bags sacks - 8.75 q.l. + 6,75 lt tanks - 35 tanks canisters - 236,26 Kg
USE: Indoor / Outdoor
COLOUR: Component A (powder) Grey • Component B (liquid) White
GRANULOMETRY: ≤ 0.5 mm
YIELD: 1,7 / 1,8 kg / sqm per mm of thickness
EN 1015-19 STEAM PASSAGE RESISTANCE COEFFICIENT: μ ≤ 22
CAPILLARY WATER ABSORPTION EN 1015-18: Class "W1"
THERMAL CONDUCTIVITY EN 1745: λ10, dry, mat = 0.79W / mK
EN 1542 ADHERENCE BOND: > 1.5 MPa
ASSORB. CAPILLARY AND WATER PERMEABILITY (w) EN 1062-3: <0,1 Kg / (m² • h⁰'⁵)
PERMEABILITY TO WATER VAPOR (sd) EN ISO 7783-2: Class I
PERMEABILITY TO CO2 (sd, CO2) EN 1062-6: <5 m
COMPRESSION RESISTANCE TO 28 days EN 1015-11: > 28 MPa (CSIV Class)

MALVIN NET 2.25

Malvin NET 2.25
Glass fibre net with anti-alcohol treatment with light mesh 25x25 mm with a weight of 225 gr / m made up of an English twist and fitted to withstand alkanes of cement and gypsum anhydride. Ideal for reinforcement and reinforcement of plasters and smoothing and structural reinforcement of walls. Specific for reinforcement system with INTORAS BICO.

PACKAGING: Rolls height 1 m Length 50 m - 25x25 mm mesh
MEDIUM THICKNESS UNI 9311/3: 3 mm
BREAST EXTENDED UNI 9311/5: 3.2%
STRENGTHENING UNDER TRACTION UNI 9311/5: Warp:> 2.500 N / 5cm • Weft:> 4.000 N / 5cm
MEDIUM THICKNESS OF FABRIC OPENED UNI 9311/3: 1.00 mm

INTORAS

Intoras
Pre-mixed fibre-reinforced anti-carbonate shrinking agent in compliance with EN 1504-2 and EN 998-1 based on special hydraulic binders, gray or natural white for external and internal smoothing of concrete surfaces, rustic and plastic coatings and / or minerals, of traditional or premixed plasters based on lime, lime and cement both new and old, even if painted, provided they are in excellent condition, of plasters with shrinkage lesions, with hand application, with smooth or sponge finish with maximum thickness of application up to 2.5 cm.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
COLOUR: Grey / White
AVAILABILITY: INTORAS G / B: max thickness of application 5 mm • INTORAS MAX G / B: max thickness of application 2.5 cm
GRANULOMETRY: Type G / B: ≤ 0.6 mm • Type MAX G / B: ≤ 1.3 mm
YIELD: 1.5 / 1.6 kg / sqm per mm of thickness
EN 1015-19 STEAM PASSAGE RESISTANCE COEFFICIENT: μ ≤ 22
CAPILLARY WATER ABSORPTION EN 1015-18: Class "W1"
THERMAL CONDUCTIVITY EN 1745: λ10, dry, mat = 0.41 W / mK
EN 1542 ADERENCE TIE: > 1 MPa
ABSORB. CAPILLARY AND WATER PERMEABILITY (w) EN 1062-3: <0,1 Kg / (m² • h⁰'⁵)
PERMEABILITY TO WATER VAPOR (sd) EN ISO 7783-2: Class I
PERMEABILITY TO CO2 (sd, CO2) EN 1062-6: > 50 m
COMPRESSION RESISTANCE At 28 days EN 1015-11: > 18 MPa (CSIV Class)

INTORAS I

Intoras PC
Pre-mixed water-repellent, anti-carbonate, fibre-reinforced, shrinkage-resistant, shrinkage layer in compliance with EN 1504-2 and EN 998-1, based on special hydraulic binders, gray or natural white for external and internal shaving of concrete surfaces, rustic and plastic coatings and / or minerals, of traditional or premixed plasters based on lime and cement, both new and old, even if painted, in excellent condition, of plasters with shrinkage lesions, applied by hand, with a smooth or sponged finish with a maximum thickness of application up to 2.5 cm.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
COLOUR: Grey / White
AVAILABILITY: INTORAS G / B: max thickness of application 5 mm • INTORAS MAX G / B: max thickness of application 2.5 cm
GRANULOMETRY: Type G / B: ≤ 0.6 mm • Type MAX G / B: ≤ 1.3 mm
YIELD: 1.5 / 1.6 kg / sqm per mm of thickness
RESISTANCE COEFFICIENT TO STEAM TRANSFER EN 1015-19: μ <22
CAPILLARY WATER ABSORPTION EN 1015-18: "W2" class
THERMAL CONDUCTIVITY EN 1745: λ10, dry, mat = 0.41 W / mK
EN 1542 ADERENCE TIE:> 1 MPa
ABSORB. CAPILLARY AND WATER PERMEABILITY (w) EN 1062-3: <0,1 Kg / (m² • h⁰'⁵)
PERMEABILITY TO WATER VAPOR (SD) EN ISO 7783-2: Class I
PERMEABILITY TO CO2 (SD, CO2) EN 1062-6:> 50 m
COMPRESSION RESISTANCE At 28 days EN 1015-11:> 18 MPa (CSIV Class)

INTORIS G

Intoris G
Premixed mortar with compensated shrinkage based on special hydraulic binders according to EN 1504-3 class R1-CC, fibre-reinforced with a special polypropylene fibber composition specially designed to be used to fill the spaces between the prefabricated panels.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
Colour: Grey
GRANULOMETRY: ≤ 1.3 mm
Yield: 1.6 kg per liter of volume to be filled
EN 1542 ADHERENCE BOND: > 0.8 MPa
CAPILLARY ABSORPTION EN 13057: ≤ 0,5 kg / (m² • h⁰'⁵)
COMPRESSION RESISTANCE TO 28 days EN 12190: ≥ 12.5 MPa (Class R1)

INTORIS I

Intoris I
Premixed pourable mortar with compensated, expansive shrinkage, based on special hydraulic binders according to EN 1504-6 specific for precision anchoring of machinery and grouting of metal structures and prefabricated elements on floors in concrete and reinforced concrete or otherwise on solid supports. To be used also in combination with selected aggregates. Available with "R3" pressure resistance ≥ 35 N / mm, type "R4" 
≥ 50N/mm.

PACKAGING: 25 kg sacks - 70 bags sacks - 17.50 ql
USE: Indoor / Outdoor
COLOUR: Grey
GRANULOMETRY: ≤ 3 mm
YIELD: 1.9 kg per lt of volume to be filled
COMPRESSION RESISTANCE TO 28 days EN 12190: Type R3: ≥ 35 N / mm
Type R4: ≥ 50 N/mm²

BETON

Beton
Based on premixed anti-shrink hydraulic binders for inside and outside with high and constant quality to be applied mechanically or by hand for the reconstruction or restoration of reinforced concrete or concrete structures or as structural consolidation of old masonry. It does not corrode metals but protects them if it covers them completely. Available fibre-reinforced with a special composition of specially designed polypropylene fibres - type "FR". Available with compression resistance class 10/17/25/35/40 N / mm², to be combined with the MALVIN NET structural reinforcement system, which uses pre-formed GFRP (Glass Fibre Reinforced Polymer) nets, connectors and accessories (* FIBRE NET), or FRP (Fibre Reinforced Polymer) nets made of AR GLASS (alkaline-resistant) glass fiber and cold drawn AISI 304 stainless steel connectors of MALVIN Srl, applied by hand or machine and kneaded with only added d water, with a consumption of 17/18 kg / m2 per cm of thickness, with a compressive strength of 28 N between 10 N / mm² and 45 N / mm² (CSIV).

PACKAGE:Loose in silo - 25 kg sacks - 70 bags sacks - 17.50 ql
USE:Indoor / Outdoor
COLOUR:Grey
GRANULOMETRY:≤ 1.3 mm
YIELD:17/18 kg / sqm
COMPRESSION RESISTANCE EN 998-1:
• R10: ≥ 10 MPa • CS IV
• R17: ≥ 17 MPa • CS IV
• R25: ≥ 25 MPa • CS IV
• R35: ≥ 35 MPa • CS IV
• R40: ≥ 45 MPa • CS IV
CAPILLARY ABSORPTION EN 13057:W1
THERMAL CONDUCTIVITY EN 1745:λ10, dry, mat = 0.43 W / mK
REACTION TO FIRE:Class A1
CLASSIFICATION UNI EN 998-31:GP-CS IV- W1